The Injection Molding Process

最も重要な事実の概要

  • TPE plastics can be processed on standard injection molding machines for thermoplastics.
  • THERMOLAST® K compounds enable longer residence times if this is required.
  • Due to the structural viscosity of TPS, these compounds are among the materials with the greatest potential in relation to the range of the processing window.

What general requirements have to be met when using TPEs in injection molding?

In general, materials from KRAIBURG TPE are free-flowing granules. These can be processed on standard injection molding machines for thermoplastics. The three-zone screws should have a compression ratio of at least 2:1 and an L/D ratio of at least 20. Processing with open nozzles is possible; working with shut-off nozzles is advantageous.

THERMOLAST® K compounds enable longer residence times if this is required. Short residence times should be the general aim, especially in the hot runner system. Care needs to be taken to ensure that the volume of the hot runner system does not exceed one to two times the shot weight.

How high should the injection speed be set?

Injection pressure and injection speed are determined by factors such as the design of the item and gate as well as the structural viscosity of the material and may vary according to the compound. For structurally viscose plastics, the cavity should be filled at a high injection speed. This makes it possible to achieve long flow paths even for very thin-walled components.

How is the filling study carried out?

The filling study begins when the machine is started at a medium rate and without holding pressure. Depending on the article’s geometry, an injection profile may also be effective. The shot volume is increased in steps of ten percent, starting from half of the calculated volume. This ensures efficiency of the ejectors.

Find the right TPE solution for your application


Making sure you get the best results: the right materials solutions have been developed for each of your specific applications.

 

See our products

How is the solidification point determined?

The solidification point is determined using a combination of holding pressure time and holding pressure level. The holding pressure only serves to compensate for processing shrinkage and not to fill the item. Starting with a holding pressure of 40 to 60 percent of the injection pressure achieved at the changeover point, the holding pressure time is increased step by step without overpacking the mold. The weight is determined after each shot. 

If no further change can be detected, the solidification point has been reached and the holding pressure phase has been completed. After assessing the item quality, this process can be repeated at higher holding pressures. It may also make sense to use holding pressure profiles.

Optimization of residual melt cushion

The residual melt cushion ensures neat pressure transmission during the holding pressure phase. It should be kept as small as possible. An optimum residual melt cushion is 10 to 15 percent of the screw diameter.

Share this post

Related Posts

Featured Knowledge Article

The Co-extrusion Process

Unlocking Innovation: The Power of the Co-extrusion Process
Thermoplastic elastomers (TPE) are an indispensable tool used by processors, product developers and designers alike. They combine the dynamic processing properties of thermoplastic plastics with the softness and flexibility of elastomers.
Featured Knowledge Article

The Extrusion Process

How are TPE processed during extrusion processes?
Thermoplastic elastomers (TPE) are an indispensable tool used by processors, product developers and designers alike. They combine the dynamic processing properties of thermoplastic plastics with the softness and flexibility of elastomers.
Featured Knowledge Article

TPUとは何ですか?

熱可塑性ポリウレタン | Thermoplastic Polyurethane (TPU)
熱可塑性ポリウレタン(TPU)は熱可塑性エラストマーのサブカテゴリーを形成しています。一般的には、これらの材料はポリエーテルやポリエステルと従来のポリウレタンのブロック共重合体です。 
Featured Knowledge Article

TPOとは何ですか?

熱可塑性ポリオレフィン | Thermoplastic polyolefins
熱可塑性ポリオレフィン(TPO)は、オレフィン系熱可塑性樹脂(PPなど)と非架橋エラストマー(EPDMなど)の混合物か、ソフトセグメントとハードセグメントを持つオレフィンコポリマーである。この材料は熱可塑性エラストマーのサブグループを形成する。
Featured Knowledge Article

TPC材料とは何ですか?

熱可塑性ポリエステルエラストマー(TPC)です (Thermoplastic polyester elastomers)
熱可塑性ポリエステル・エラストマー(TPC)は、ポリエステルとポリエーテルのブロック共重合体です。TPCは熱可塑性エラストマーのサブグループを形成しています。
Featured Knowledge Article

TPA材料とは何ですか?

熱可塑性ポリアミドエラストマー(TPA)です (Thermoplastic polyamide elastomers)
熱可塑性ポリアミドエラストマー(TPA)は、ポリアミドとエーテル化合物、またはポリアミドとエステル化合物をベースにしたブロック共重合体です。ポリマー鎖において、ポリアミド(PA6など)は硬質相を形成し、エーテル化合物またはエステル化合物は弾性特性のための軟質相を形成します。TPAは熱可塑性エラストマーのサブグループを形成しています。
Featured Knowledge Article

TPSとはどのようなものですか?

熱可塑性スチレンブロックコポリマー(TPS)です (Thermoplastic styrene block copolymers) (TPS)
熱可塑性スチレン・ブロック・コポリマー(TPS)は、熱可塑性エラストマー(TPE)のサブグループの一つです。 
Featured Knowledge Article

TPVとは何ですか?

熱可塑性加硫エラストマ | Thermoplastic vulcanizates (TPV)
TPVは熱可塑性加硫エラストマーの略称です。TPVは、主にポリプロピレンとEPDMをベースとした材料であり、弾力性があり熱可塑性材料としての加工が可能です。一般的な熱可塑性エラストマー(TPE)グループののサブカテゴリーを形成しています。